The effect of light rare earth element substitution in Yb14MnSb11 on thermoelectric properties

Author affiliations

Abstract

After the discovery of Yb14MnSb11 as an outstanding p-type thermoelectric material for high temperatures (≥900 K), site substitution of other elements has been proven to be an effective method to further optimize the thermoelectric properties. Yb14−xRExMnSb11 (RE = Pr and Sm, 0 < x < 0.55) compounds were prepared by powder metallurgy to study their thermoelectric properties. According to powder X-ray diffraction, these samples are iso-structural with Yb14MnSb11 and when more than 5% RE is used in the synthesis the presence of (Yb,RE)4Sb3 is apparent after synthesis. After consolidation and measurement, (Yb,RE)Sb and (Yb,RE)11Sb10 appear in the powder X-ray diffraction patterns. Electron microprobe analysis results show that consolidated pellets have small (Yb,RE)Sb domains and that the maximum amount of RE in Yb14−xRExMnSb11 is x = 0.55, however, (Yb,RE)11Sb10 cannot be distinguished by electron microprobe analysis. By replacing Yb2+ with RE3+, one extra electron is introduced into Yb14MnSb11 and the carrier concentration is adjusted. Thermoelectric performance from room temperature to 1275 K was evaluated through transport and thermal conductivity measurements. The measurement shows that Seebeck coefficients initially increase and then remain stable and that electrical resistivity increases with substitutions. Thermal conductivity is slightly reduced. Substitution of Pr and Sm leads to enhanced zT. Yb13.82Pr0.18Mn1.01Sb10.99 has the best maximum zT value of ∼1.2 at 1275 K, while Yb13.80Sm0.19Mn1.00Sb11.02 has its maximum zT of ∼1.0 at 1275 K, respectively, ∼45% and ∼30% higher than Yb14MnSb11 prepared in the same manner.

Graphical abstract: The effect of light rare earth element substitution in Yb14MnSb11 on thermoelectric properties

Back to tab navigation

Supplementary files

Publication details

The article was received on 29 Jul 2015, accepted on 31 Jul 2015 and first published on 31 Jul 2015


Article type: Paper
DOI: 10.1039/C5TC02326B
Author version
available:
Download author version (PDF)
Citation: J. Mater. Chem. C, 2015,3, 10566-10573
  •   Request permissions

    The effect of light rare earth element substitution in Yb14MnSb11 on thermoelectric properties

    Y. Hu, S. K. Bux, J. H. Grebenkemper and S. M. Kauzlarich, J. Mater. Chem. C, 2015, 3, 10566
    DOI: 10.1039/C5TC02326B

Search articles by author

Spotlight

Advertisements