Pressure induced thermoelectric enhancement in SnSe crystals

Abstract

SnSe crystals are excellent thermoelectric materials due to their high ZT value (∼2.6 along the b direction) at high temperature ∼923 K. However, in the temperature range of 300–773 K, the ZT values are just 0.1–0.9. To make this material more efficient, its thermoelectric properties should be large in the entire temperature range. Here, we use computational methods to show how pressure intrinsically enhances the thermoelectric properties below 700 K along the three directions (a, b and c) of the crystal (the low-T SnSe-Pnma phase) due to the significant electrical transport boost. The estimated ZT values of p-type materials along the b and c directions can reach as high as 2.5 and 1.7 at 6 GPa and 700 K, respectively. At 6 GPa, the a direction shows potential n-type behavior with a ZT value of 1.7 at 600 K. It is significant that high performance for both n-type and p-type conductors could be available in SnSe just through applying pressure. Our work on SnSe under pressure sheds light on a new mechanism to enhance the thermoelectric properties of materials.

Graphical abstract: Pressure induced thermoelectric enhancement in SnSe crystals

Article information

Article type
Paper
Submitted
01 May 2016
Accepted
30 Jun 2016
First published
05 Jul 2016

J. Mater. Chem. A, 2016,4, 12073-12079

Pressure induced thermoelectric enhancement in SnSe crystals

Y. Zhang, S. Hao, L. Zhao, C. Wolverton and Z. Zeng, J. Mater. Chem. A, 2016, 4, 12073 DOI: 10.1039/C6TA03625B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements