Freeze-dried WS2 composites with low content of graphene as high-rate lithium storage materials
Few layered WS2–graphene nanosheet composites are prepared by a simple and scalable hydrothermal reaction and a subsequent freeze-drying method. The freeze-dried WS2–graphene composite exhibits good cycling stability and outstanding high-rate capability of lithium storage. The reversible capacity remains 647 mA h g−1 after 80 cycles at a current density of 0.35 A g−1. Comparable capacities of 541 and 296 mA h g−1 can still be maintained when cycling at even higher current densities of 7 and 14 A g−1 (7 and 14 mA cm−2) respectively.