Porous carbon nanosheets with precisely tunable thickness and selective CO2 adsorption properties

Abstract

We report the wet-chemistry synthesis of a new type of porous carbon nanosheet whose thickness can be precisely controlled over the nanometer length scale. This feature is distinct from conventional porous carbons that are composed of micron-sized or larger skeletons, and whose structure is less controlled. The synthesis uses graphene oxide (GO) as the shape-directing agent and asparagine as the bridging molecule that connects the GO and in situ grown polymers by electrostatic interaction between the molecules. The assembly of the nanosheets can produce macroscopic structures, i.e., hierarchically porous carbon monoliths which have a mechanical strength of up to 28.9 MPa, the highest reported for the analogues. The synthesis provides precise control of porous carbons over both microscopic and macroscopic structures at the same time. In all syntheses the graphene content used was in the range 0.5–2.6 wt%, which is significantly lower than that of common surfactants used in the synthesis of porous materials. This indicates the strong shape-directing function of GO. In addition, the overall thickness of the nanosheets can be tuned from 20 to 200 nm according to a fitted linear correlation between the carbon precursor/GO mass ratio and the coating thickness. The porous carbon nanosheets show impressive CO2 adsorption capacity under equilibrium, good separation ability of CO2 from N2 under dynamic conditions, and easy regeneration. The highest CO2 adsorption capacities can reach 5.67 and 3.54 CO2 molecules per nm3 pore volume and per nm2 surface area at 25 °C and ∼1 bar.

Graphical abstract: Porous carbon nanosheets with precisely tunable thickness and selective CO2 adsorption properties

Supplementary files

Article information

Article type
Paper
Submitted
05 Jun 2013
Accepted
11 Oct 2013
First published
14 Oct 2013

Energy Environ. Sci., 2013,6, 3740-3747

Porous carbon nanosheets with precisely tunable thickness and selective CO2 adsorption properties

G. Hao, Z. Jin, Q. Sun, X. Zhang, J. Zhang and A. Lu, Energy Environ. Sci., 2013, 6, 3740 DOI: 10.1039/C3EE41906A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements