Author affiliations

Abstract

The direct utilization of carbonaceous fuels is examined in a solid oxide fuel cell (SOFC) with a molten Sb anode at 973 K. It is demonstrated that the anode operates by oxidation of metallic Sb at the electrolyte interface, with the resulting Sb2O3 being reduced by the fuel in a separate step. Although the Nernst Potential for the Sb-Sb2O3 mixture is only 0.75 V, the electrode resistance associated with molten Sb is very low, approximately 0.06 Ωcm2, so that power densities greater than 350 mW cm−2 were achieved with an electrolyte-supported cell made from Sc-stabilized zirconia (ScSZ). Temperature programmed reaction measurements of Sb2O3 with sugar char, rice starch, carbon black, and graphite showed that the Sb2O3 is readily reduced by a range of carbonaceous solids at typical SOFC operating conditions. Finally, stable operation with a power density of 300 mW cm−2 at a potential of 0.5 V is demonstrated for operation on sugar char.

Graphical abstract: A direct carbon fuel cell with a molten antimony anode

Back to tab navigation
Please wait while Download options loads

Publication details

The article was received on 31 May 2011, accepted on 11 Jul 2011 and first published on 11 Aug 2011


Article type: Paper
DOI: 10.1039/C1EE01863A
Citation: Energy Environ. Sci., 2011,4, 4133-4137
  •   Request permissions

    A direct carbon fuel cell with a molten antimony anode

    A. Jayakumar, R. Küngas, S. Roy, A. Javadekar, D. J. Buttrey, J. M. Vohs and R. J. Gorte, Energy Environ. Sci., 2011, 4, 4133
    DOI: 10.1039/C1EE01863A

Search articles by author