Propagation of nanopores during anodic etching of n-InP in KOH

Author affiliations

Abstract

We propose a three-step model of electrochemical nanopore formation in n-InP in KOH that explains how crystallographically oriented etching can occur even though the rate-determining process (hole generation) occurs only at pore tips. The model shows that competition in kinetics between hole diffusion and electrochemical reaction determines the average diffusion distance of holes along the semiconductor surface and this, in turn, determines whether etching is crystallographic. If the kinetics of reaction are slow relative to diffusion, etching can occur at preferred crystallographic sites within a zone in the vicinity of the pore tip, leading to pore propagation in preferential directions. Symmetrical etching of three {111}A faces forming the pore tip causes it to propagate in the (remaining) 〈111〉A direction. As a pore etches, propagating atomic ledges can meet to form sites that can become new pore tips and this enables branching of pores along any of the 〈111〉A directions. The model explains the observed uniform width of pores and its variation with temperature, carrier concentration and electrolyte concentration. It also explains pore wall thickness, and deviations of pore propagation from the 〈111〉A directions. We believe that the model is generally applicable to electrochemical pore formation in III–V semiconductors.

Graphical abstract: Propagation of nanopores during anodic etching of n-InP in KOH

Back to tab navigation
Please wait while Download options loads

Publication details

The article was received on 28 May 2013, accepted on 17 Jul 2013 and first published on 31 Jul 2013


Article type: Paper
DOI: 10.1039/C3CP52253A
Citation: Phys. Chem. Chem. Phys., 2013,15, 15135-15145
  •   Request permissions

    Propagation of nanopores during anodic etching of n-InP in KOH

    R. P. Lynch, N. Quill, C. O'Dwyer, S. Nakahara and D. N. Buckley, Phys. Chem. Chem. Phys., 2013, 15, 15135
    DOI: 10.1039/C3CP52253A

Search articles by author