3-D flower-like NiCo alloy nano/microstructures grown by a surfactant-assisted solvothermal process

Abstract

Uniform 3-D flower-like NiCo crystalline nano/microstructures were synthesized by a surfactant-assisted solvothermal process at 120 °C for 10–15 h, which were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), energy dispersive X-ray spectroscopy (EDX) and vibrating sample magnetometry (VSM). The effects of synthetic parameters such as surfactant, solvent and molar ratio of metal ions on the formation and morphology of NiCo samples were investigated. The experimental results showed that sodium dodecylbenzenesulfonate (SDBS) and solvent ethanol play critical roles in the formation of novel flower-like NiCo alloy assemblies, and the self-assembly evolution was found to be a two-stage growth process. Magnetic hysteresis measurements revealed that the flower-like Ni48Co52 alloy spheres with an average diameter of ca. 800 nm and hierarchical flower-like Ni47Co53 alloys with a size of ca. 5 μm display ferromagnetic behaviors with saturation magnetizations of 111.33 emu g−1 and 103.58 emu g−1, and coercivities of 84.27 Oe and 52.71 Oe, respectively, at room temperature.

Graphical abstract: 3-D flower-like NiCo alloy nano/microstructures grown by a surfactant-assisted solvothermal process

Supplementary files

Article information

Article type
Paper
Submitted
29 Jul 2010
Accepted
11 Oct 2010
First published
05 Nov 2010

CrystEngComm, 2011,13, 1328-1332

3-D flower-like NiCo alloy nano/microstructures grown by a surfactant-assisted solvothermal process

X. Wei, X. Zhou, K. Wu and Y. Chen, CrystEngComm, 2011, 13, 1328 DOI: 10.1039/C0CE00468E

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements