Modification of SBA-15 pore connectivity by high-temperature
Abstract
Two-dimensional hexagonally ordered CMK-3 carbons were
synthesized using SBA-15 templates calcined at a temperature of 1153 K,
whereas a disordered carbon was obtained using SBA-15 calcined at 1243 K,
demonstrating that the pores connecting ordered mesopores in SBA-15