Redox-triggered hydrogels revealing switchable stiffness properties and shape-memory functions

Author affiliations

Abstract

The synthesis, characterization and application of redox-switchable hydrogels are described. The first system includes the crosslinking of terpyridine-functionalized acrylamide copolymer chains by redox-active metal-ion terpyridine complexes (Mn/n+1 = Ru2+/3+; Os2+/3+). The redox state of the complexes bridging the hydrogel controls the stiffness of the resulting hydrogels. The Ru2+-terpyridine polyacrylamide hydrogel reveals enhanced stiffness (G′ = 110 Pa) compared to the Ru3+-terpyridine bridged hydrogel that exhibits lower stiffness (G′ = 50 Pa). By the cyclic oxidation and reduction of the hydrogel with persulfate and dopamine, respectively, reversible switching of the hydrogel stiffness is demonstrated. Similarly, the Os3+-terpyridine-crosslinked hydrogel reveals lower stiffness (G′ = 30 Pa) compared to the Os2+-terpyridine-bridged hydrogel (G′ = 45 Pa). By the reversible oxidation and reduction of the Os2+/3+ with sodium persulfate and ascorbic acid, the switchable stiffness of the hydrogel is demonstrated. The second system involves metal-ion-crosslinked carboxymethylcellulose hydrogels (Mn+1/n = Fe3+/2+; Ru3+/2+). The reduced metal-ion-crosslinked hydrogels Fe2+-carboxymethylcellulose (formed in the presence of ascorbic acid) and the Ru2+-carboxymethylcellulose (formed in the presence of dopamine) exhibit lower stiffness values corresponding to 80 Pa and 320 Pa, respectively, while high-stiffness Fe3+- and Ru3+-carboxymethylcellulose hydrogels (formed in the presence of sodium persulfate) are observed, G′ = 210 Pa and 460 Pa, respectively. The reversible redox-stimulated switching of the stiffness of the hydrogels is demonstrated. In addition, carboxymethylcellulose chains modified with self-complementary nucleic acid tethers are crosslinked by two cooperative crosslinkers consisting of Fe3+/2+-carboxylate and DNA duplexes. The resulting Fe3+-carboxymethyl cellulose/duplex nucleic acid-bridged hydrogel exhibits high stiffness, G′ = 210 Pa, whereas the Fe2+-carboxymethylcellulose/duplex DNA reveals substantially lower stiffness, G′ = 80 Pa. The hydrogel reveals reversible shape-memory properties.

Graphical abstract: Redox-triggered hydrogels revealing switchable stiffness properties and shape-memory functions

Back to tab navigation

Supplementary files

Publication details

The article was received on 04 Apr 2018, accepted on 18 Apr 2018 and first published on 23 Apr 2018


Article type: Paper
DOI: 10.1039/C8PY00515J
Citation: Polym. Chem., 2018, Advance Article
  •   Request permissions

    Redox-triggered hydrogels revealing switchable stiffness properties and shape-memory functions

    M. Fadeev, G. Davidson-Rozenfeld, Y. Biniuri, R. Yakobi, R. Cazelles, M. A. Aleman-Garcia and I. Willner, Polym. Chem., 2018, Advance Article , DOI: 10.1039/C8PY00515J

Search articles by author

Spotlight

Advertisements