Skutterudite with graphene-modified grain-boundary complexion enhances zT enabling high-efficiency thermoelectric device

Author affiliations

Abstract

Skutterudite materials are widely considered for thermoelectric waste heat recovery. While the skutterudite structure effectively scatters the high frequency phonons, grain-boundary engineering is needed to further reduce the thermal conductivity beyond simply decreasing grain size. Here, we show that reduced graphene oxide (rGO) increases the grain boundary thermal resistivity by a factor of 3 to 5 compared to grain boundaries without graphene. Wrapping even micron sized grains with graphene leads to such a significant reduction in the thermal conductivity that a high thermoelectric figure of merit zT = 1.5 was realized in n-type YbyCo4Sb12, while a zT of 1.06 was achieved in p-type CeyFe3CoSb12. A 16 leg thermoelectric module was made by using n- and p-type skutterudite–graphene nanocomposites that exhibited conversion efficiency 24% higher than a module made without graphene. Engineering grain boundary complexions with 2-D materials introduces a new strategy for advanced thermoelectric materials.

Graphical abstract: Skutterudite with graphene-modified grain-boundary complexion enhances zT enabling high-efficiency thermoelectric device

Back to tab navigation

Supplementary files

Publication details

The article was received on 24 Aug 2016, accepted on 17 Oct 2016 and first published on 04 Nov 2016


Article type: Paper
DOI: 10.1039/C6EE02467J
Citation: Energy Environ. Sci., 2017,10, 183-191
  •   Request permissions

    Skutterudite with graphene-modified grain-boundary complexion enhances zT enabling high-efficiency thermoelectric device

    P. Zong, R. Hanus, M. Dylla, Y. Tang, J. Liao, Q. Zhang, G. J. Snyder and L. Chen, Energy Environ. Sci., 2017, 10, 183
    DOI: 10.1039/C6EE02467J

Search articles by author

Spotlight

Advertisements