Preparation of solid silver nanoparticles for inkjet printed flexible electronics with high conductivity

Author affiliations

Abstract

Silver nanoparticles (NPs) which could be kept in solid form and were easily stored without degeneration or oxidation at room temperature for a long period of time were synthesized by a simple and environmentally friendly wet chemistry method in an aqueous phase. Highly stable dispersions of aqueous silver NP inks, sintered at room temperature, for printing highly conductive tracks (∼8.0 μΩ cm) were prepared simply by dispersing the synthesized silver NP powder in water. These inks are stable, fairly homogeneous and suitable for a wide range of patterning techniques. The inks were successfully printed on paper and polyethylene terephthalate (PET) substrates using a common color printer. Upon annealing at 180 °C, the resistivity of the printed silver patterns decreased to 3.7 μΩ cm, which is close to twice that of bulk silver. Various factors affecting the resistivity of the printed silver patterns, such as annealing temperature and the number of printing cycles, were investigated. The resulting high conductivity of the printed silver patterns reached over 20% of the bulk silver value under ambient conditions, which enabled the fabrication of flexible electronic devices, as demonstrated by the inkjet printing of conductive circuits of LED devices.

Graphical abstract: Preparation of solid silver nanoparticles for inkjet printed flexible electronics with high conductivity

Back to tab navigation
Please wait while Download options loads

Supplementary files

Publication details

The article was received on 15 Oct 2013, accepted on 15 Nov 2013 and first published on 20 Nov 2013


Article type: Paper
DOI: 10.1039/C3NR05479A
Citation: Nanoscale, 2014,6, 1622-1628
  •   Request permissions

    Preparation of solid silver nanoparticles for inkjet printed flexible electronics with high conductivity

    W. Shen, X. Zhang, Q. Huang, Q. Xu and W. Song, Nanoscale, 2014, 6, 1622
    DOI: 10.1039/C3NR05479A

Search articles by author