V5+ degradation of sulfonated Radel membranes for vanadium redox flow batteries

Author affiliations

Abstract

Insight into the degradation mechanisms of aromatic proton conducting membrane separators for vanadium redox flow batteries (VRFBs) is urgently needed for the development of long lifetime VRFBs. Other than in-cell observations of performance degradation, there is little fundamental evidence on the specific degradation pathways of aromatic ion exchange membranes for VRFBs. Herein we investigated a sulfonated Radel® membrane (S-Radel) as the degradation target to study the degradation mechanism of aromatic polymers by V(V) (or generally V5+) oxidation. It was found that the ductile S-Radel membrane, which has a similar aromatic backbone structure to the most-studied polyaromatic VRFB membranes that have shown high performance, became brittle and discolored after 3 days of immersion in 1.7 M V(V) + 3.3 M H2SO4 solution at 40 °C. The membrane's intrinsic viscosity was reduced to about half of its original value after this exposure to V(V) while the ion exchange capacity did not change. In addition to chain scission, it was found that –OH groups were introduced to the backbone of S-Radel as the major degradation product. Quinone groups were also observed at 1677 cm−1 in FTIR measurements. While the V(V) species in VRFBs is usually denoted as VO2+, V(V)[double bond, length as m-dash]O in VOCl3 was found to not have degradation activity for S-Radel. Therefore, we hypothesized that there were other reactive forms of V(V) species that first attacked the S-Radel by incorporating hydroxyl groups into the polymer's aromatic backbone, followed by the oxidation of these hydroxyl groups to quinone functionalities through a redox mechanism.

Graphical abstract: V5+ degradation of sulfonated Radel membranes for vanadium redox flow batteries

Back to tab navigation

Supplementary files

Publication details

The article was received on 14 May 2013, accepted on 23 May 2013 and first published on 23 May 2013


Article type: Paper
DOI: 10.1039/C3CP52035H
Citation: Phys. Chem. Chem. Phys., 2013,15, 11299-11305
  •   Request permissions

    V5+ degradation of sulfonated Radel membranes for vanadium redox flow batteries

    D. Chen and M. A. Hickner, Phys. Chem. Chem. Phys., 2013, 15, 11299
    DOI: 10.1039/C3CP52035H

Search articles by author

Spotlight

Advertisements