Swelling-induced mesoporous block copolymer membranes with intrinsically active surfaces for size-selective separation

Abstract

Block copolymers (BCPs) are receiving growing interest in the preparation of advanced membranes with regular pores due to their capability to form highly ordered, mesoscopic structures via microphase separation. We report on the fabrication of composite membranes with mesoporous amphiphilic BCPs as the size-selective layer and a macroporous membrane as the supporting layer by coating BCPs onto the supporting membrane. Mesopores were generated in the BCP layer by a selective swelling-induced pore-formation process. The composite membranes showed high pore regularity, strong mechanical robustness, and a separating property that can be tuned simply by changing the swelling time. Furthermore, the polyelectrolyte-natured blocks were exclusively relocated on the pore surface of the BCP layer during the swelling process, rendering an intrinsically active surface on the membrane. As a result, the hydrophilicity and fouling resistance of the membranes were significantly enhanced, and the membranes possessed a reversible pH-sensitive water flux. The membranes were used to separate nanoparticles of similar sizes and it was observed that the membrane subjected to 24 h of swelling was able to discriminate 10 nm gold particles from a mixture containing 2 nm gold particles with ∼100% yield, demonstrating its superior size selectivity.

Graphical abstract: Swelling-induced mesoporous block copolymer membranes with intrinsically active surfaces for size-selective separation

Supplementary files

Article information

Article type
Paper
Submitted
03 Jul 2012
Accepted
17 Aug 2012
First published
17 Aug 2012

J. Mater. Chem., 2012,22, 20542-20548

Swelling-induced mesoporous block copolymer membranes with intrinsically active surfaces for size-selective separation

Z. Wang, X. Yao and Y. Wang, J. Mater. Chem., 2012, 22, 20542 DOI: 10.1039/C2JM34292H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements