Solubility-driven polythiophene nanowires and their electrical characteristics

Abstract

We demonstrated that interconnected nanofibrillar networks of poly(3-hexylthiophene) (P3HT) thin films with improved crystallinity can be easily fabricated by aging the precursor solution with marginal solvent. Structural analysis revealed that these benefits arise from the improvements in the crystallinity of P3HT in the precursor solution. At dilute concentrations, P3HT molecules grew into near-spherical particles during the aging time. As the aging time increased further, P3HT molecules exhibited one-dimensional growth into rod-like structures. At higher P3HT concentrations and longer P3HT solution aging times, dense nanowires were observed to form gradually, thereby improving the electronic properties of field-effect transistors (FETs) based on these films. This improvement was due to the change in P3HT organization in the precursor solution from a random-coil conformation to an ordered aggregate as a result of aging in a marginal solvent, methylene chloride. At high temperatures, the P3HT molecules were completely solvated and adopted a random-coil conformation, as is observed in good solvents. Whereas upon aging the solution at room temperature, methylene chloride poorly solvated the P3HT molecules such that ordered aggregates of P3HT grew in solution, which improved the molecular ordering of P3HT thin films produced from these solutions. The field-effect mobility of the thin films was, therefore, enhanced without the need for post-treatments.

Graphical abstract: Solubility-driven polythiophene nanowires and their electrical characteristics

Article information

Article type
Paper
Submitted
16 Sep 2010
Accepted
10 Nov 2010
First published
21 Dec 2010

J. Mater. Chem., 2011,21, 2338-2343

Solubility-driven polythiophene nanowires and their electrical characteristics

Y. D. Park, S. G. Lee, H. S. Lee, D. Kwak, D. H. Lee and K. Cho, J. Mater. Chem., 2011, 21, 2338 DOI: 10.1039/C0JM03114C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements